Hi all, We are working on a fast and easy second surface mount and would love to get your feed back before we go into production. All we need is a 8-1/2" X 11" to test Final size 8" X 10". We have been working on this for years and think we are set to go but would like to get some critical...

We were the collateral damage in a typo years ago. A travel agent sent a mailing to every employee at Kodak offering a great price on a cruise. He printed our 800 # on it. Monday morning the phone started ringing off the hook. I got the first calls and had one of them fax me the flyer. I...

Signage is correct. Alcohol will harden the rollers over time. If you must use a product/solution to clean with something like blanket wash used to clean offset printing blankets work and will rejuvenate the roller. Graphic Laminating has a product for cleaning Heat film not sure if it will work...

As an equipment guy for both hot and cold laminators we always recommend opening the rolls when not in use but not because of flat bands on the roll. A well made roller the correct silicone rubber at the correct durometer should not develop a flat band on the rollers. But if you stop it with...

I think you are reading the SS # Not the Model # looks like a Econocraft 60" What do you want to know?

Shot in the dark, is the bottom roll driving, more than likely yes. Is it slipping on the ink therefore not feeding to the next pass of the inkjet head as far thus making the print shorter. IE the traction on the media is better than on the ink.

Most dry-erase film is OPP Oriented Polypropylene. The surface tension is good for a dry-erase corona treatment improves the product. A higher treatment level and the ink sticks better, too high and it is difficult to get off cleanly. Too low a surface tension and the marker beads up. Some...